Polayên kêm-alloy Flux têl binavkirî E81T1-B2C Welding stuff
KOMPONETA KÎMYYA:
ALLOY(wt%) | C | Mn | Si | Cr | V | Mo | P | S |
GB / T RULES | 0,05-0,12 | 1.25 | 0.80 | 1.00-1.50 | - | 0,40-0,65 | 0.03 | 0.03 |
AWS RULES | 0,05-0,12 | 1.25 | 0.80 | 1.00-1.50 | - | 0,40-0,65 | 0.03 | 0.03 |
MÎNAK NIRX | 0.052 | 0.88 | 0.28 | 1.12 | 0.105 | 0.46 | 0.009 | 0.005 |
TAYBETÎ MÊKANÎK:
MAL | HÊZA BERHEMÊ (MPa) | XWEZAYÊ BERÊRÊKIRIN (MPa) | NIRXA IMAPACT J/℃ | DIRÊZ (%) | Tedawiya germê ° Cxh | |||||
GB / T RULES | 470 | 550-690 | - | 17 | 730*2 | |||||
AWS RULES | 470 | 550-690 | - | 19 | 730*2 | |||||
MÎNAK NIRX | 560 | 640 | 50 / Germahiya normal | 23 | 730*2 |
PÊŞNÎŞAN PARAMETÊN WELDING:
DIAMETERS SPECIFICATIONS(mm) | 1.2 | ||||
Wolt | 24-35 | ||||
Amp | 160-320 | ||||
Dirêjahiya dirêjkirina hişk (mm) | 15-20 | ||||
Herikîna gazê (l/min) | 15-25 |
Arc nerm û bi îstîqrar e, kêm dilopek, xweşik çêdibe.
Rakirina slag baş, soot kêmtir.
Bi performansa pêvajoya weldingê ya hêja.
-
Projeya etilenê 1 mîlyon ton / sal Parzûnkirina Zhenhai
-
Materyalên welding ji bo otomobîlên rêwîtiyê
-
JU2000E jack-up sondajê
KOMPONETA KÎMYYA:
ALLOY(wt%) | C | Mn | Si | Cr | V | Mo | P | S |
GB / T RULES | 0,05-0,12 | 1.25 | 0.80 | 1.00-1.50 | - | 0,40-0,65 | 0.03 | 0.03 |
AWS RULES | 0,05-0,12 | 1.25 | 0.80 | 1.00-1.50 | - | 0,40-0,65 | 0.03 | 0.03 |
MÎNAK NIRX | 0.052 | 0.88 | 0.28 | 1.12 | 0.105 | 0.46 | 0.009 | 0.005 |
TAYBETÎ MÊKANÎK:
MAL | HÊZA BERHEMÊ (MPa) | XWEZAYÊ BERÊRÊKIRIN (MPa) | NIRXA IMAPACT J/℃ | DIRÊZ (%) | Tedawiya germê ° Cxh | |||||
GB / T RULES | 470 | 550-690 | - | 17 | 730*2 | |||||
AWS RULES | 470 | 550-690 | - | 19 | 730*2 | |||||
MÎNAK NIRX | 560 | 640 | 50 / Germahiya normal | 23 | 730*2 |
PÊŞNÎŞAN PARAMETÊN WELDING:
DIAMETERS SPECIFICATIONS(mm) | 1.2 | ||||
Wolt | 24-35 | ||||
Amp | 160-320 | ||||
Dirêjahiya dirêjkirina hişk (mm) | 15-20 | ||||
Herikîna gazê (l/min) | 15-25 |